Oxidation of silicon nanoparticles produced by ns laser ablation in liquids
2014
The investigation of nanoparticles produced by ns pulsed Nd:YAG laser ablation of silicon in liquids is reported. Combined characterization by morphological and structural techniques shows that these nanoparticles have a mean diameter of ~3 nm and a core-shell structure consisting of a Si-nanocrystal surrounded by a layer of oxidized Si. Time resolved luminescence spectra evidence visible and UV emissions: a broad band around 1.9 eV originates from Si-nanocrystals, while two bands centered at 2.7 eV and 4.4 eV are associated with oxygen deficient centers in the SiO2 shell.
Homogeneous and inhomogeneous contributions to the luminescence linewidth of point defects in amorphous solids: Quantitative assessment based on time…
2008
The article describes an experimental method that allows to estimate the inhomogeneous and homogeneous linewidths of the photoluminescence band of a point defect in an amorphous solid. We performed low temperature time-resolved luminescence measurements on two defects chosen as model systems for our analysis: extrinsic Oxygen Deficient Centers (ODC(II)) in amorphous silica and F+ 3 centers in crystalline Lithium Fluoride. Measurements evidence that only defects embedded in the amorphous matrix feature a dependence of the radiative decay lifetime on the emission energy and a time dependence of the first moment of the emission band. A theoretical model is developed to link these properties to…
Defect-related visible luminescence of silica nanoparticles
2013
The high photon emissivity in the visible spectral range is one of the most relevant phenomena emerging from the reduction of silica down to nanoscale; hence it is promising for the development of optical nanotechnologies (down converter, probes, display). It is well accepted that the origin of this luminescence is related to the high specific surface (~100 m2/g) that favors the formation of optically active defects at the nanosilica surface. With the aim to clarify the role of specific luminescent defects, here we report a detailed study of spectral and decay features by time-resolved photoluminescence spectra under a visible-UV tunable laser excitation. Our study is carried out on differe…
Nano-Oxides produced by ns laser ablation in liquids
2014
Laser ablation in liquids was successfully applied to produce nanosized oxides from Si, Ti and Zn targets. The obtained colloidal solutions of nanoparticles were investigated by complementary techniques: AFM, IR and Raman spectroscopies; optical absorption and time resolved photoluminescence. The results demonstrate the production of SiO2, TiO2 and ZnO. The absorption and emission properties of these material have been also investigated and appear to be promising for optical applications.
Visible luminescence peculiar to sintered silica nanoparticles: Spectral and decay properties
2015
We report that the sintering at 1000 degrees C of silica nanoparticles (an average diameter of 14 nm) produces a transparent sample that exhibits a bright visible emission under UV excitation. The use of time resolved luminescence spectroscopy and a tunable laser source allows us to single out three contributions centered at 1.96 eV, 2.41 eV and 3.43 eV. The excitation spectra of these emissions evidence bell shaped bands consistent with transitions between localized defects' states. For each emission we study the intensity and the lifetime in the temperature range from 300 K down to 10 K, thus evidencing the competition between radiative and non-radiative processes in the optical cycle of …
Luminescence properties induced by sintering of silica nanoparticles
2014
The effect of sintering on the optical properties of silica nanoparticles, a mean diameter of ~14 nm, are investigated by absorption and luminescence experiments. The sintering is induced by a thermal treatment of 1000 °C for 272 hours; after that the sample is transparent, and emits a bright luminescence under UV excitation. Time resolved photoluminescence spectra excited by a tunable laser source allows to evidence four bands around 2.0 eV, 2.4 eV, 2.7 eV and 3.4 eV, peculiar to defects induced by the sintering.